Many questions about my new watch



 
 
Thread Tools Display Modes
  #1  
Old July 2nd 05, 08:18 AM
external usenet poster
 
Posts: n/a
Default Many questions about my new watch

I got an Omega Seamaster Chrono Diver 300M about a month and a half
ago, and I have a couple questions and comments about my experience
with it:

-Some parts of the watch case and bracelet are rhodium plated. I
noticed after a couple days that there were ultra-fine 'scratches',
more like 'rainbow reflections' on the rhodium plating. Then after a
few weeks, they multiplied into hundreds of very fine scratches, some
sort of big, all over the rhodium. They are usually only visible at
certain angles, but since there are so many, it really dulls the
appearance of the rhodium. I have no idea where the scratches are
coming from. I clean the watch weekly in a tub of warm water and mild
car wash soap, and a soft toothbrush, followed by drying with cotton
terry towels. Why is Rhodium and Stainless Steel (the SS also has MANY
scuff marks and scratches) so easy to scratch? The watch almost never
touches my clothes or anything else.

-How can I get the rhodium looking like new again? Is replating
possible if the watch is not ALL rhodium plated? Some parts of the case
are rhodium plated, most is bare stainless steel. Also, the bracelet
links have little rhodium parts in them. Is this replatable somehow?
Does the rhodium get attracted only to other bits of rhodium during the
electroplating process?

-What is the best way to prevent scratches and clean the watch? I would
have no problem using some kind of ultrasound cleaner or what have you.
Can ultrasound cleaners be used on mechanical movement watches like
this one? This watch also has a sapphire crystal, would it shatter if
exposed to ultrasound?

-The stainless steel has many scuff marks, can these be buffed out?
Part of the bracelet, the clasp, has what looks like laser engraved
writing, would buffing it wear down the edges of the writing and make
it look softer?

-Is there some way I could buff the rhodium and the stainless steel
myself and remove the scratches? Maybe a dremel like tool or something
with some kind of abrasive compound?

Thanks everyone!


Ads
  #2  
Old July 2nd 05, 10:09 AM
Abrasha
external usenet poster
 
Posts: n/a
Default

wrote:
I got an Omega Seamaster Chrono Diver 300M about a month and a half
ago, and I have a couple questions and comments about my experience
with it:

-Some parts of the watch case and bracelet are rhodium plated. I
noticed after a couple days that there were ultra-fine 'scratches',
more like 'rainbow reflections' on the rhodium plating. Then after a
few weeks, they multiplied into hundreds of very fine scratches, some
sort of big, all over the rhodium. They are usually only visible at
certain angles, but since there are so many, it really dulls the
appearance of the rhodium. I have no idea where the scratches are
coming from. I clean the watch weekly in a tub of warm water and mild
car wash soap, and a soft toothbrush, followed by drying with cotton
terry towels. Why is Rhodium and Stainless Steel (the SS also has MANY
scuff marks and scratches) so easy to scratch? The watch almost never
touches my clothes or anything else.


Both Rhodium and Stainless Steel are a lot softer than the particles in
regular dust. The fact that the watch "almost never" touches anything
is not good enough. How about that "soft" toothbrush? That scratches
it like hell. That's why jewelers use an ultrasonic machine or a
steamer to clean jewelry and not a "soft" toothbrush. And how about
those cotton terry towels, do you also call that "never touches anything
else"? Even rubbing it with your fingers will scratch it.

My point is, you are doing a fine job scratching your watch with your
tooth brush, the terry cloth, your fingers and anything else that you
touch the watch with. And I do mean anything.


-How can I get the rhodium looking like new again?


Have it repolished. This is rather difficult and time consuming (read
costly), because of the way the bracelet is constructed. The watch
needs to be taken apart to do this properly.

Take a look at
http://www.unitedwatchservices.com/. Click on
"services". Then click on "see sample" under "Renew and Repolishing"
Then click on "Men's Omega" Does this watch look familiar to you?

I strongly advice you, that until your watch looks as scratched and
abused as the one in the picture do not bother with having it repolished.

BTW, United Watch Services is my next door neighbor, so I am rather
familiar with the process.

? Is replating
possible if the watch is not ALL rhodium plated? Some parts of the case
are rhodium plated, most is bare stainless steel. Also, the bracelet
links have little rhodium parts in them. Is this replatable somehow?


Sure, just show me the money. We love customers like you. Actually we
do not, because after a few weeks you'll be back complaining that the
watch is scratched again even though "almost nothing ever touches it".
Except your tooth brush and those terry cloth towels of course.

Does the rhodium get attracted only to other bits of rhodium during the
electroplating process?

-What is the best way to prevent scratches


Place the watch in a dust proof case, and never take it out. Never
touch it with anything at all. Just look at it. Treat it as if it were
in a museum. Most definitely, do not wear it. Wearing it is the surest
way to scratch it.

and clean the watch?



I would
have no problem using some kind of ultrasound cleaner or what have you.


Pointless if you decide to wear the watch.

Can ultrasound cleaners be used on mechanical movement watches like
this one?


Sure, go ahead.

This watch also has a sapphire crystal, would it shatter if
exposed to ultrasound?


That would have to be one hell of an ultrasonic cleaner.


-The stainless steel has many scuff marks, can these be buffed out?


Yes.

Part of the bracelet, the clasp, has what looks like laser engraved
writing, would buffing it wear down the edges of the writing and make
it look softer?


Yes, especially if you do this often enough.


-Is there some way I could buff the rhodium and the stainless steel
myself and remove the scratches?


Sure, we love guys like you. Then when you fail, we make more money
trying to fix what you screwed up.

In all seriousness, you can do this yourself. Just make sure that you
get the proper equipment first, as well as the proper training to gain
the knowledge how to polish stainless steel, as well as how to do this
without destroying your watch.

Maybe a dremel like tool or something
with some kind of abrasive compound?


Dremel tool? That is not the proper equipment I was talking about.
Abrasive compound? I thought you wanted to remove the scratches.


Thanks everyone!


You're welcome.

One piece of advice. Just wear and enjoy your new watch and get over
it, that it is getting scratched. That is perfectly normal. The only
substance in the world that does not get scratched is a diamond.
Everything else gets scratched. Just get over it.

Abrasha
http://www.abrasha.com

  #3  
Old July 3rd 05, 05:12 PM
m4816k
external usenet poster
 
Posts: n/a
Default

wrote in message
...
I got an Omega Seamaster Chrono Diver 300M about a month and a half
ago, and I have a couple questions and comments about my experience
with it:

-Some parts of the watch case and bracelet are rhodium plated. I
noticed after a couple days that there were ultra-fine 'scratches',
more like 'rainbow reflections' on the rhodium plating. Then after a
few weeks, they multiplied into hundreds of very fine scratches, some
sort of big, all over the rhodium. They are usually only visible at
certain angles, but since there are so many, it really dulls the
appearance of the rhodium. I have no idea where the scratches are
coming from. I clean the watch weekly in a tub of warm water and mild
car wash soap, and a soft toothbrush, followed by drying with cotton
terry towels. Why is Rhodium and Stainless Steel (the SS also has MANY
scuff marks and scratches) so easy to scratch? The watch almost never
touches my clothes or anything else.

-How can I get the rhodium looking like new again? Is replating
possible if the watch is not ALL rhodium plated? Some parts of the case
are rhodium plated, most is bare stainless steel. Also, the bracelet
links have little rhodium parts in them. Is this replatable somehow?
Does the rhodium get attracted only to other bits of rhodium during the
electroplating process?

-What is the best way to prevent scratches and clean the watch? I would
have no problem using some kind of ultrasound cleaner or what have you.
Can ultrasound cleaners be used on mechanical movement watches like
this one? This watch also has a sapphire crystal, would it shatter if
exposed to ultrasound?

-The stainless steel has many scuff marks, can these be buffed out?
Part of the bracelet, the clasp, has what looks like laser engraved
writing, would buffing it wear down the edges of the writing and make
it look softer?

-Is there some way I could buff the rhodium and the stainless steel
myself and remove the scratches? Maybe a dremel like tool or something
with some kind of abrasive compound?

Thanks everyone!


Have you considered asking your jeweller to make a satin or matte finish on
the watch? It will still scratch, but scratches will be much less visible.
It's not really a great sollution cause the watch would look somewhat
different, but if you don't tolearte scratches... I'm also like that, love
to keep things brand new. But it's best to learn to enjoy things instead of
searching for microscopic scratches:-) By the way, when you polish a metal's
surface it's scratched right away (cause polishing is "done by scratching")
but scratches are so little that you don't even notice. Regards!



 




Thread Tools
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

vB code is On
Smilies are On
[IMG] code is On
HTML code is Off
Forum Jump

Similar Threads
Thread Thread Starter Forum Replies Last Post
Question -- Benrus Watch [email protected] Jewelry 0 January 3rd 05 09:37 AM
Peyote Watchband Questions Diana Curtis Beads 19 October 11th 04 05:34 PM
The ten questions I want you to answer Jalynne Beads 19 June 22nd 04 08:58 PM
AD: Watch Faces Marisa Exter Beads 2 April 15th 04 09:59 PM
How Do I Fix My Watch Battery? Stephanie Jewelry 11 October 14th 03 04:22 PM


All times are GMT +1. The time now is 08:32 PM.


Powered by vBulletin® Version 3.6.4
Copyright ©2000 - 2024, Jelsoft Enterprises Ltd.