nJb wrote:
....
I would suggest colloidal silica instead of waterglass.
Is that not just the same stuff by different names?
We had a thread
about that when I built my kiln last year. One trade name is Kaowool
Rigidizer, made just for what you're doing. Also, using the pleated
process for lining the glory hole reduces loose fiber.
I don't know that process or I may have difficulties translating
it. Can you elaborate on that?
Paai
|