Shiny facest
I usually put a coat of TLS on the faces of my figures to smooth things out
and fill in any imperfections and it gives a nice smooth matte finish to the faces. Well today I decided to mix in a little diluent to let it flow on and level off a little better but when I pulled it out of the oven I had extremly high gloss faces which I did NOT want. So I thought I'd ask if anyone has run into this before, maybe you Katherine? So a heads up on any one who doesn't want shiny faces.( I'm putting a light coat of just TLS on top of it to see if I can tone down the shine.) Dawn Stubitsch http://www.thumbprintkids.com |
Dawn---you are saying that TLS plus diluent is shiny when baked?....... I
don't have any diluent to try that--would you pretty please repeat your experiment on a little scrap and see if indeed its that mix that caused the shiny effect? If it is, guess I better get some... Sarajane Sarajane's Polymer Clay Gallery http://www.polyclay.com |
Very intriguing!!... I echo Sarajane's call for more experimenting.
It would be great if we had the option of giving Translucent Liquid Sculpey a shiny finish whenever we wanted it (for transfers, etc., even though we wouldn't want them on faces...lolol). Might it even work for original opaque-white LS too?? How much Diluent do you think you added (proportionally) to the TLS? |
I just tried it again but this batch didn't turn out shiny so I'm increasing
the amount of dilent. I was only mixing a tiny amount since I was just painting a couple of small faces. The amount may have been as much as half and half , I'm just not sure but it was extremely high gloss when it came out. When you don't want something to happen, it does. When you try...go figure! I'm still trying. -- Dawn Stubitsch http://www.thumbprintkids.com http://www.thumbprintkids.com/pages/caketoppers.htm http://www.thumbprintkids.com/pages/photoguidlines.htm "DianeGlassAttic" wrote in message ... Very intriguing!!... I echo Sarajane's call for more experimenting. It would be great if we had the option of giving Translucent Liquid Sculpey a shiny finish whenever we wanted it (for transfers, etc., even though we wouldn't want them on faces...lolol). Might it even work for original opaque-white LS too?? How much Diluent do you think you added (proportionally) to the TLS? |
The amount may have been as much as half
and half , I'm just not sure but it was extremely high gloss when it came out. was it touching anything? I know baking touching tiles or glass makes clay shiney...but these are scuplted faces, dimensional, right? so that can't be it... I do appreciate your scientific bent, here! Sarajane Sarajane's Polymer Clay Gallery http://www.polyclay.com |
The figures were standing upright touching nothing. I've been trying to get
it to happen again on pieces of baked clay, even raw clay, but I can't. The heads were up toward the upper heating coil but I believe that only comes on during the broil cycle but if it had it would have scorched the figures. I've tried several different ratios of clay to diluent..nothing. I tried to increase the temperature and the length of time...no change. SOMETHING happened and it's driving me nuts. Dawn Stubitsch http://www.thumbprintkids.com http://www.thumbprintkids.com/pages/caketoppers.htm http://www.thumbprintkids.com/pages/photoguidlines.htm "Sjpolyclay" wrote in message ... The amount may have been as much as half and half , I'm just not sure but it was extremely high gloss when it came out. was it touching anything? I know baking touching tiles or glass makes clay shiney...but these are scuplted faces, dimensional, right? so that can't be it... I do appreciate your scientific bent, here! Sarajane Sarajane's Polymer Clay Gallery http://www.polyclay.com |
SOMETHING
happened and it's driving me nuts. did you have anything different on your hands when you made them, ie lotion, gloves?? Sarajane Sarajane's Polymer Clay Gallery http://www.polyclay.com |
Nope! Nothing out of the ordinary. I didn't even touch the faces except with
the brush which is used exclusively for TLS. ???? Dawn Stubitsch http://www.thumbprintkids.com http://www.thumbprintkids.com/pages/caketoppers.htm http://www.thumbprintkids.com/pages/photoguidlines.htm "Sjpolyclay" wrote in message ... SOMETHING happened and it's driving me nuts. did you have anything different on your hands when you made them, ie lotion, gloves?? Sarajane Sarajane's Polymer Clay Gallery http://www.polyclay.com |
Dawn, was anything else in the oven with it?
Maybe you have checked all the baking variables , though I'm still wondering about a short temp flux---high heat does sometimes melt the clay into shiny-ness before scorching it. Next would be the clay itself---was it sitting around, or fresh out of the wrapper? Did you try the reoccuring experimental pieces out of the very same clay? Sarajane Sarajane's Polymer Clay Gallery http://www.polyclay.com |
This was the final bake just to add the TLS.. Everything had already been
baked several times. I used the same method for baking as I always do and had done on this figure. They were alone in the oven and I was using the same batch of clay that other figures had come from. The I tried a higher temperature bake on some test clay. The clay was scorched around the edges but the area that I applied the TLS mix to was still matte. -- Dawn Stubitsch http://www.thumbprintkids.com http://www.thumbprintkids.com/pages/caketoppers.htm http://www.thumbprintkids.com/pages/...0guidlines.htm "Sjpolyclay" wrote in message ... Dawn, was anything else in the oven with it? Maybe you have checked all the baking variables , though I'm still wondering about a short temp flux---high heat does sometimes melt the clay into shiny-ness before scorching it. Next would be the clay itself---was it sitting around, or fresh out of the wrapper? Did you try the reoccuring experimental pieces out of the very same clay? Sarajane Sarajane's Polymer Clay Gallery http://www.polyclay.com |
All times are GMT +1. The time now is 12:46 AM. |
|